MCQ
The statement that is $INCORRECT$ about the interstitial compound is
- Athey have metallic conductivity
- Bthey have high melting points
- ✓they are chemically reactive
- Dthey are very hard
✓
Answer
Correct option: C.
they are chemically reactive
c
In case of interstial compounds there is presence of small atoms (or impurity) in the lattice of metal. So interstial compounds are hard, high melting point and chemically inert.
In case of interstial compounds there is presence of small atoms (or impurity) in the lattice of metal. So interstial compounds are hard, high melting point and chemically inert.
Need a full question paper?
Generate a complete, print-ready paper with questions like this in minutes — across 16+ boards, with answer keys.
Explore more
Similar questions
$0.02\,mole$ of $[Co(NH_3)_5Br]Cl_2$ and $0.02\,mole$ of $[Co(NH_3)_5Cl]SO_4$ are present in $200 \,cc$ of a solution $X$. The number of moles of the precipitates $Y$ and $Z$ that are formed when the solution $X$ is treated with excess silver nitrate and excess barium chloride are respectively
→Which of the following sets of reagents, used in the order shown, would successfully accomplish the conversion shown ?
Complex compound $[Co(SCN)_2(NH_3)_4]Cl$ does not exhibit
→A catalyst lowers the activation energy for a certain reaction from $83.314$ to $75 \,KJ\,mol^{-1}$ at $500\,K$ . What will be the rate of reaction as compare to uncatalysed reaction ? Assume other things being equal ....... $times$
→When ethane $-1, 2-$ dioic acid is heated with conc. $H_2SO_4$, it gives
→Identify $X$ and $Y$
→At normal temperature iodoform is
The electrodes of a conductivity cell are $3\,cm$ apart and have a cross-sectional area of $4\,c{m^2}$. The cell constant of the cell (in $c{m^{ - 1}}$) is
→Which of the following alkene cannot be prepared by de-amination of $n-Bu- NH_2$ with $NaNO_2/HCl$ ?
→During the electrolysis of molten sodium chloride, the time required to produce $0.10\, mol$ of chlorine gas using a current of $3$ amperes is .......... $\min.$
→